Of man-made fibers: — Other (229)
Part of: 590691 — Other: — Knitted or crocheted:
844357 · 2000-08-10 — The tariff classification of six styles of wet suit material from Japan.
Six samples were submitted. All consist of knit polyester jersey fabrics that have been laminated on one or both sides to a either neoprene rubber sheeting or to hyplon sheeting, which for tariff purposes is considered a plastics material. You state the following composition for these fabrics: STYLE RUBBER/PLASTIC POLYESTER JERSEY 1mm Neoprene* 61% 39% 1.5mm Neoprene* 71% 29% 2mm Hyplon* 78% 22% 3mm Hyplon 82% 18% 3mm Smooth Skin (rubber) 82% 18% 3mm Textured Skin (rubber) 82% 18% Three samples* were sent to our internal laboratory which found the following: STYLE RUBBER/PLASTIC POLYESTER…
f85350 · 2000-04-28 — The tariff classification of woven and knit upholstery fabrics both containing either a plastic or rubber back coating, from India.
The supplier is Reliance Industries Ltd., India. Six samples were submitted, which included one each of the woven and knit fabrics both before and after the plastics or rubber coatings were applied. The first set of samples, identified as style 7599, consists of a dobby woven fabric of yarns of different colors having the following fiber composition by weight: 43% Filament polyester (textured) 7% Spun polyester (carded) 42% Spun acrylic (carded) 8% Spun viscose (carded) The yarn size in the warp is 1/155/34/250 filament polyester and the yarn size in the filling is 2/21 acrylic + 2/7…
816333 · 1995-12-08 — The tariff classification of a rubberized textile fabric for use in the manufacture of men's shirts, from either Hong Kong or Korea.
The instant sample, which was identified as style #CNHY347, consists of a tricot knit nylon fabric that has been laminated on one surface with a gray pigmented rubber film. This material, which is for use in the manufacture of shirts, was analyzed by the New York Customs laboratory which made the following determination concerning weights: Wt. of textile fabric: 2.9oz/y2 (99.9g/m2) Wt. of rubber: 1.9oz/y2 (64.7g/m2) Total wt.: 4.8oz/y2 (164.6g/m2) The applicable subheading for the material will be 5906.91.2500, Harmonized Tariff Schedule of the United States (HTS), which provides for…
894644 · 1994-03-03 — The tariff classification of eight styles of neoprene rubber sheets for making fishing waders and scuba diving wet suits, from Taiwan.
We note per a recent telephone conversation that the manufacturer of these sheets is CR-UNO Indust. Co. Ltd., of Taiwan. While three representative samples were submitted, you request the tariff classification of eight materials in all. No weight specifications were furnished. All of these materials will be imported in sheet sizes measuring 50" wide x 87" long. The first sample, measuring 2.0mm in thickness, consists of a layer of neoprene rubber which has been laminated on one side with a knit fabric of nylon man-made fiber construction. The second submitted sample measuring 3.0mm in…